    POE best "O" ring material



    Hi,

    what is the best choice of "O" ring material for POE lubricated systems (wide temp range)

    (Wrigleys does not count)

    thanks

    Mad



  2. #2
    Join Date
    Dec 2007
    Location
    australia
    Posts
    3,356
    Rep Power
    39

    Re: POE best "O" ring material

    MF Sabroe seen to use HNBR for everything, so suggest to check on compatability chart.

  3. #3
    Join Date
    Sep 2007
    Location
    Somerset
    Age
    69
    Posts
    4,758
    Rep Power
    46

    Re: POE best "O" ring material

    Mad fridgie.

    Ranger is on the case.
    Read the attached all will be revealed.
    Grizzly

    O-ring Materials
    NITRILE or BUNA N (NBR) MEDIUM NITRILE
    TEMP RANGE -40°C to +110°C with excursion to +135°C
    Resistance to mineral based fluids is excellent, although resistance to fuels is not usually good enough. Strength, resistance, abrasion and heat resistance are reasonable. Low temperature resistance is adequate for most applications but weathering or ozone contact will result in crazing and cracking, particularly under tensile stress or flexure. This grade of nitrile is the most commonly used of all polymers in hydraulic sealing

    Recommended for:
    • General purpose sealing
    • Petroleum oils and fluids
    • Cold water
    Not Recommended for:
    • Halogenated Hydrocarbons (Carbon Tetrachloride Trichlorethylene)
    • Nitro Hydrocarbons (Nitrobenzene, Aniline)
    • Phosphate Ester Hydraulic Fluids (Skydrol, Fyrquel, Pydraul)
    • Ketones (MEK, Acetone)
    • Strong Acids
    • Ozone
    • Automotive Brake Fluid

    HIGH NITRILE
    TEMPT RANGE -30°C to =I IO°C
    Resistance to mineral based fluids is excellent and to hydrocarbon fuels is good. Strength, resilience abrasion and high temperature resistance are reasonable but performance at low temperature is poor.
    Primarily used in contact with aromatic fuels and mineral oils.

    LOW NITRILE
    TEMP RANGE -50°C to =I IO°C
    Low Nitrile has some resistance to mineral based fluids but the main advantage is its low temperature capability. Strength, resilience and abrasion resistance are reasonable.
    Note: It is important to remember that all Nitriles are non-resistant to castor based and non-mineral brake fluids and should never be used in applications employing these fluids.

    FLUOROCARBON RUBBER
    TEM PRANGE -20°c to +200°c
    Commonly known as FPM (alternative to Viton ® Du Pont & Dow Elastomers). It has high temperature capabilities, excellent resistance to hydraulic oils, petrols and many chemicals ,including weathering and ozone conditions.
    Fluorocarbon O-Rings should be considered for seal use in automobile and other mechanical devices requiring maximum resistance to elevated temperature and to many functional fluids.

    Recommended for use with:
    • Petroleum Oils
    • Di ester Based Lubricants
    • Silicate Ester Base Lubricants
    • Silicone Fluids and Greases
    • Halogenated Hydrocarbons (Carbon Tetrachloride. Trichloro - Ethylene)
    • Selected Phosphate Ester Fluids
    • Acids
    Not recommended for use with:
    • Ketones
    • Skydrol fluids
    • Amines, Anhydrous Ammonia
    • Hot hydrofluoric or Chlorosulfonic Acids

    SILICONE RUBBER
    TEMP RANGE -65°C to +250°C
    Silicone has poor tensile strength, tear resistance and abrasion resistance Silicones possess excellent resistance to temperature extremes. Silicone's retention of properties at high temperatures is superior to other elastic materials.

    Silicones are recommended for:
    • Dry heat
    • High - aniline point oils
    • Chlorinated DI - phenyls
    • Food processing applications
    • Excellent ozone resistance.
    • Water (Low temperature only)
    Silicones are not recommended for:
    • Most Petroleum fluids
    • Ketones (MEK, Acetone)
    • Steam.

    FLUOROSILICON
    TEMP RANGE -60°C to +180°C
    Higher grade of Silicone (usually blue) recommended for applications involving Hydrocarbon Oils, Petroleum Fuels and mineral based Hydraulic Fluids. This material experiences similar mechanical limitations to Silicone.

    ETHYLENE PROPYLENE RUBBER (EPR or EPDM)
    TEMP RANGE -50°c to +125°c
    Excellent resistance to weathering and ozone, water and steam, with good performance in castor and some phosphate ester based fluids. It's low and high temperature capability is good, having excellent resistance to set with good resilience.
    Boiling water and steam are considered among the most difficult conditions to seal and until the introduction of EPDM around 1961 no adequate clastomeric material was available, This polyiner is now used to a large extent in central heating systems replacing the outdated gland material. Also high temperature braking systems employing castor based fluids for mouldings subjected to weathering and ozone and for seals in chemical plant due to its good chemical resistance.
    It should NEVER be used in contact with mineral based fluids or DI ester based lubricants, due to excessive swell and deterioration.
    When lubrication is required silicone grease or fluids should be used.

    P.T.F.E. POLYTETRAFLUORETHYLENE
    TEMP RANGE -195°c to +250°c
    P.T.F.E. is an extremely inert material and is unaffected by virtually every known chemical including almost all acids, alkalis and solvents.
    These exceptional properties make P.T.F.E. an ideal material for O-ring Back up Rings. It's cold flow characteristics under permanent strain are usually a disadvantage in P.T.F.E. O-Rings, e.g. It has little memory to return to its original form.

    F.E.P. ENCAPSULATED O-RINGS FPM (alternative to Viton ® Du Pont & Dow Elastomers) or SILICONE
    F.E.P. FPM TEMP RANGE -20°C to +204°C F.E.P. SILICONE TEMP RANGE -60°C to +204°C
    An encapsulated O-ring comprises an elastomer energising core, which has a seamless jacket made from fluoropolymer.
    The elastomeric core may be Fluorocarbon (FPM or Silicone. The jacket is made from Teflon®
    Du PontF.E.P. (Fluorinated - ethylene - propylene).
    Why are Encapsulated 'O-Rings needed?
    There are certain applications which prohibit the use of conventional rubber O-ring Seals. The use of hostile chemicals or extreme temperature (both high and low) during various processes can make effective sealing very difficult.
    The main advantage Encapsulated 'O-Rings have over solid P.T.F.E. is that it has the chemical inertness whilst with its energising core, the O-ring returns to its original form.

    Recommended for use in:
    • Chemical Processing and Production
    • Oil Extraction (on shore and off shore)
    • Petrochemical Refining
    • Pharmaceutical Production
    • Food and Drink Processing
    • Paint and Die Manufacturing
    • Cosmetics and Perfumery
    • Automotive Components
    • Aerospace Engineering
    Not Recommended for:
    • Dynamic use where high speeds and poor finishes are encountered.
    • Where the housing design requires excessive stretch or collapse of the O-ring during installation.



    KALREZ ® Du Pont & Dow Elastomers
    TEMP RANGE -50°C to +315°C
    This material has outstanding chemical resistance and a temperature capability up to +350°C (intermittent). Wherever rubber components are exposed to aggressive chemicals or high temperatures Kalrez
    ® Perfluoroelastomer parts last longer. Kalrez®parts have virtually universal chemical resistance. They are far more resistant to swelling, a key cause of seal failure, and other forms of chemical attack than other lastomers. Kalrez® has the chemical inertness of P.T.F.E. and the elasticity of rubber.

  4. #4
    Join Date
    Aug 2009
    Location
    New Zealand
    Age
    59
    Posts
    2,556
    Rep Power
    26

    Re: POE best "O" ring material

    thanks you young fellows!

  5. #5
    Join Date
    Dec 2007
    Location
    australia
    Posts
    3,356
    Rep Power
    39

    Re: POE best "O" ring material

    KALREZ is a good "0" ring at between $100 each for a small one & price goes upwards from there!

  6. #6
    Join Date
    May 2006
    Location
    India
    Age
    74
    Posts
    400
    Rep Power
    18

    Re: POE best "O" ring material

    Epdm is known to be delivering a good performance

  7. #7
    Join Date
    Dec 2007
    Location
    australia
    Posts
    3,356
    Rep Power
    39

    Re: POE best "O" ring material

    Quote Originally Posted by D.D.KORANNE View Post
    Epdm is known to be delivering a good performance
    I would not use it on anything as it does not like oil ie mineral based or DI ester based lubricants.

    see Grizzly's "0" ring chart.

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •